| 摘要 |
PURPOSE:To improve the dimensional stability of a molded articles by compounding a resin component comprising a polyamide resin and a modified polyolefin, the ratio of melt flow rate of the polyamide to the polyolefin being in a specified range, with a glass fiber and an inorg. flaky filler. CONSTITUTION:80-50wt.% polyamide resin and 20-50wt.% modified polyolefin which is partly or completely modified with an unsatd. acid, the ratio of the melt flow rate of the polyamide to that of the polyolefin being 0.5 or higher, are compounded to give a resin component. 75-50wt.% of the component is compounded with 10-40wt.% glass fiber comprising chopped strand glass usually produced as a reinforcement for a resin and having a mean fiber diameter of 5-20mum and a mean fiber length of 0.5-10mm and 15-40wt.% inorg. flaky filler (e.g. mica). |