Processing method of non-woven intrinsically with enhanced deodorant feature from bamboo

摘要

The present invention provides a processing method of non-woven intrinsically with enhanced deodorant feature from bamboo. The process uses mixture of wasted coffee residue and bamboo pulp as raw material. The process uses N-methylmorpholine N-oxide (NMMO) as primary solvent and 1, 3-phenylene-bis 2-oxazoline (BOX) as additive stabilizer. A cellulose solution is firstly formed by the wasted coffee residue, bamboo pulp, NMMO and BOX aforesaid. Secondly, via grinding, blending, dissolving and thermal dehydrating, the cellulose solution is converted into spinning dope. Thirdly, via meltblown method, the dope is extruded out of spinnerets in a die assembly by a metering gear pump to form thread bundle. Finally, the thread bundle is orderly treated by coagulation with regeneration via ejecting mist aerosol of water, rinsing, bleaching, re-rinsing, drying, winding-up and the like to create continuous filaments, then final product for nonwoven with deodorant feature is produced by the filaments from bamboo cellulose.

主权项

1. A method for producing a continuous filament for making non-woven fabrics with enhanced deodorant features, wherein the method comprises the following steps:
a. blending bamboo pulp and wasted coffee residue together into a mixture, wherein the bamboo pulp comprises cellulose having a degree of polymerization (DP) from 400-800, and the wasted coffee residue has been ground into particles with a diameter of 500 nm-1000 nm; b. adding N-methylmorpholine N-oxide (NMMO) as a dissolving solvent and 1,3-phenylene-bis 2-oxazoline (BOX) as an additive stabilizer into the mixture of step a. and blending and dissolving the mixture at a temperature of 50° C.-70° C. using a horizontal dope blending machine to form a slurry; c. dehydrating the slurry of step b. by vacuum thin film evaporation (VTFE) and heating at a temperature of 80° C.-100° C. to form a mucilaginous dope; d. extruding the mucilaginous dope of step c. out of spinnerets by a meltblown method to form a thread bundle; and e. treating the thread bundle of step d. by rinsing with water, bleaching, drying and winding-up to create a continuous filament for making non-woven fabrics with enhanced deodorant features.