| 摘要 |
1,230,254. Wire-reinforced float glass. ERSTE DEUTSCHE FLOATGLAS & CO. OHG. G.m.b.H. 11 June, 1969 [14 June, 1968], No. 29561/69. Heading C1M. In the manufacture of float glass, a wire inlay is introduced downwards into the glass strip when it is at a temperature of about 1050‹ C. by means of a wire inlay guiding means which is maintained clear of the glass surface and the surface of the glass downstream from the point of introduction is heated to ensure an even plane surface. As shown in Fig. 1, molten glass 1 is cast on to a bath 4 of molten tin 3 and in the first and hottest zone 3A spreads out to a glass strip 11 of width determined by side limiting bodies 5 of graphite which have a central hole (6) for the supply of cooling fluid which, if porous graphite is used, may be a protective gas or liquid tin to assist movement of the glass strip 11. In the midlde zone 3B, the tin is cooled by side cooling tubes (13) and bottom tubes 12 to maintain the glass at about 1050‹ C., the zone 3B being deeper than adjacent zones and with barriers 14 to ensure an even cooling. Above this zone, and set into roof 28 of the bath 4, is the wire inlay supply and guiding means comprising supply rolls 24, feed rolls 22, 23 and guide bodies 20, 21 all except the tips of the bodies 20, 21 being enclosed in a gas tight housing 26. After the wire inlay 10 is introduced into the strip 11, the strip passes to zone 3C where heaters 31 re-form the top surface of the glass which may otherwise show cuts from the wire inlay. As shown in Fig. 4, in zone 3B, the bodies 5 and deeper bath are replaced by a graphite barrier 41 with cooling tubes 40, the barrier 41 having projections 42 for limiting the width of the glass strip 11. The guide bodies 20, 21 are curved as shown and are provided with heat-insulated outer and bottom surfaces and are hollow with coolant flowed therethrough. To supply separate wires, the guides 20, 21 are replaced by double-walled guide tubes. The guides 20, 21 may be adjustably mounted to vary the height relative to the glass and also the inclination. As shown in Fig. 7, the body 20 may be replaced by a pair of guides 70, 71 with a space between through which hot protective gas via duct 75 is blown on to the glass strip 11 and which depresses the strip 11 and tin 3 below it to form a curve 74 so that the wire inlay 76 can be led into the strip 11 at the level required. In a further embodiment (Fig. 8, not shown), the wire inlay 76, led over guide body 21, enters the glass strip which is raised over a barrier (80), the top part (82) of which is of porous graphite and molten tin is pumped with a central hole (81) so as to pass through the barrier to give a layer (83) of tin below the raised glass layer (84). Reference has been directed by the Comptroller to Specification 1,157,406. |