AL-BASED QUASICRYSTALLINE PARTICLES AND METHOD OF PREPARING THE SAME BY SELF-FRACTURING |
摘要 |
PURPOSE: A method for preparing Al-based quasicrystalline particles by self-fracturing is provided, which can prepare Al-based quasicrystalline with a particle size of about 100 μm by self-fracturing in atmosphere at low cost. CONSTITUTION: The method includes the steps of dissolving 0.1 to 1.0 wt.% of carbon in Al-Cu-Fe based alloy or Al-Co-Ni based alloy to prepare an Al-based quasicrystalline alloy ingot; heat treating the Al-based quasicrystalline alloy ingot at 730 to 780 deg.C for 2 to 5 hrs; and exposing the Al-based quasicrystalline alloy ingot in atmosphere.
|