发明名称 |
Corrosion-inhibited iron-based members and method of producing the same |
摘要 |
A corrodible iron-based work such as a cylinder rod is subjected to hard chrome plating, heat-treatment by high frequency heating or baking at a temperature of not less than 150 DEG C. (e.g. 170 DEG to 600 DEG C.), resin impregnation treatment and finish buffing in that order to produce a corrosion-inhibited member. In the impregnation step, a thermosetting resin may be impregnated under subatmospheric pressure. After the impregnation step, the thermosettable resin or sealant may be cured in a curing step. The present invention provides for an remarkably high degree of corrosion resistance even though the thickness of the hard chrome plating layer is small.
|
申请公布号 |
US5480536(A) |
申请公布日期 |
1996.01.02 |
申请号 |
US19940265012 |
申请日期 |
1994.06.24 |
申请人 |
KOWA INDUSTRY WORKS CO., LTD. |
发明人 |
SUEHIRO, ATSUO;KOGASHIWA, NORIO |