| 摘要 |
A method for forming monotungsten carbide, comprising heating a solid, non-elemental tungsten-containing material in a flowing atmosphere containing molecular hydrogen and molecular methane for a time sufficient to convert substantially all of the tungsten-containing material to monotungsten carbide, The heating brings the temperature of the tungsten-containing material to a first elevated temperature of from about 520 to about 550 DEG C. and, subsequently, at a rate of from about 3 to about 10 DEG C. per minute, the heating brings the temperature from the first elevated temperature to a second elevated temperature of about 800 to about 900 DEG C. Thereafter the temperature is held at the second elevated temperature for at least about 15 minutes. At least about 50 weight percent of the monotungsten carbide formed is formed while holding the temperature at the second elevated temperature.
|