Active metal brazing material |
摘要 |
The present invention provides an active metal brazing material composed of a Ag—Cu—Ti—Sn alloy containing by weight 20 to 40% of Cu, 1.0 to 3.0% of Ti, 1.2 to 6.0% of Sn and the balance being Ag, and having a metallographic structure including a Sn—Ti or Cu—Ti intermetallic compound dispersed in a Ag—Cu alloy matrix, wherein the weight ratio Sn/Ti between Ti and Sn is 1.2 or more, and additionally the particle size of the intermetallic compound is 20 μm or less. The foregoing active metal brazing material improves the workability of the hitherto known Ag—Cu—Ti alloy active metal brazing material and enables a critical dimension processing with a high processing rate, and can be produced by melting and casting the foregoing Ag—Cu—Ti—Sn alloy, and by subsequently plastically working the cast at a working rate of 90% or more to make finer the intermetallic compound involved. |
申请公布号 |
US9375811(B2) |
申请公布日期 |
2016.06.28 |
申请号 |
US201214110709 |
申请日期 |
2012.05.21 |
申请人 |
TANAKA KIKINZOKU KOGYO K.K. |
发明人 |
Kishimoto Takaomi;Kashiwagi Kouzou;Sakaguchi Osamu |
分类号 |
B23K35/30;C04B37/00;C22C5/08;B23K35/40;B23K35/02;C22F1/14 |
主分类号 |
B23K35/30 |
代理机构 |
Roberts & Roberts, LLP |
代理人 |
Roberts & Roberts, LLP |
主权项 |
1. An active metal brazing material comprising a Ag—Cu—Ti—Sn alloy including 20 to 40% by weight of Cu, 1.0 to 3.0% by weight of Ti, 1.2 to 6.0% by weight of Sn and the balance being Ag, the active metal brazing material having a metallographic structure including a Sn—Ti intermetallic compound and a Sn—Ti—Cu intermetallic compound, and optionally a Cu—Ti intermetallic compound, dispersed in a Ag—Cu alloy matrix, wherein the weight ratio Sn/Ti between Ti and Sn is 1.2 or more but 5.0 or less, and the particle sizes of the intermetallic compounds are all 20 μm or less. |