ROLLING METHOD FOR LOW BRIGHTNESS STAINLESS STEEL FOIL

摘要

PURPOSE:To obtain the stainless fall having low brightness by using a lubricating oil added with specific ester and butyl stearate and specifying the surface roughness of rolls, rolling speed and draft. CONSTITUTION:The mixed long-chain dibasic acid isobutyl glycol diester expressed by formula I or the mixed cyclic dibasic acid isobutyl glycol diester expressed by formula II or the dimer acid isobutyl glycol ester expressed by formula III is added at 5wt.% into the base oil consisting of a mineral oil system having >=7cSt viscosity in the final finish rolling for producing the stainless steel foil. In addition, the butyl stearate is added at >=5% thereto to adjust the viscosity over the entire part to <=70cSt. Cold rolling is executed at >=100m/min rolling speed and >=10% draft by using such lubricating oil and using the rolls of 55mm diameter adjusted to <=0.06mum surface roughness.