| 摘要 |
<p>The present invention provides a steel plate having a low welding crack susceptibility and a yield strength of 800 MPa and a manufacturing method for the same. The steel plate having a low welding crack susceptibility comprises the following chemical components (wt.%: percent by weight): C:0.03-0.08wt.%, Si:0.05-0.70wt.%, Mn:1.30-2.20w.t%, Mo:0.10-0.30wt.%, Nb:0.03-0.10wt.%, V:0.03-0.45wt.%, Ti:0.002-0.040wt.%, Al:0.02-0.04wt.%, B:0.0010-0.0020wt.%, the balance being Fe and unavoidable impurities, and the welding crack susceptibility index meets the following formula: Pcm‰¤0.20%. The theimo-mechanical controlled rolling and cooling processes is used to obtain an ultrafine bainite batten matrix structure, which increases the intensity, plasticity and toughness of the steel plate. The steel plate with a low welding crack susceptibility of the present invention has a yield strength of greater than 800 MPa, a tensile strength of greater than 900 MPa, a Charpy impact energy Akv (-20°C) of no less than 150J and an excellent welding performance.</p> |