发明名称 |
LOW TEMPERATURE SINTERING DIELECTRIC MATERIAL |
摘要 |
PROBLEM TO BE SOLVED: To provide a low temperature sintering dielectric material which can be calcined at <=1000 deg.C and shows low dielectric loss in a high frequency region. SOLUTION: The material consists of 60 to 100 vol.% crystalline glass powder and 0 to 40 vol.% ceramic powder and has such property that the material has 95 to 100 vol.% crystal phase and 0 to 5 vol.% glass phase after calcination. |