<p>A metal nickel powder which can deliver an excellent sintering behavior during a monolithic ceramic capacitor production process and displays an excellent dispersibility when a conductive paste is formed to thereby prevent delamination; specifically, a metal nickel powder which contains 0.1 to 2.0 wt.% of oxygen, has not absorption peak in a 3600 to 3700 cm-1 wave number region of infrared absorption spectra and is generated by bringing a nickel chloride gas into contact with a reducing gas in a reducing reaction temperature region.</p> |