A method for producing a hot-dip zinc alloy coated steel sheet excellent in coating adhesion, comprising: hot-rolling a steel sheet, subjecting the base sheet for coating to a reduction heat treatment, and subjecting the base sheet for coating to hot-dip zinc alloy coating. The hot-dip alloy coated steel sheet is excellent in coating adhesion, by using, as a base sheet for coating, a steel sheet that is imparted with resistance to liquid metal embrittlement cracking by adding B. The hot-dip zinc alloy coated steel sheet excellent in coating adhesion contains at least one of a Si simple oxide, a Mn simple oxide, a Cr simple oxide, a Si—Mn composite oxide, a Si—Cr composite oxide, a Mn—Cr composite oxide, and a Si—Mn—Cr composite oxide in a portion within 10 μm from an interface between a steel sheet as a base sheet and a hot-dip galvanized layer formed on a surface thereof. |
| 主权项 |
1. A method for producing a hot-dip zinc alloy coated steel sheet excellent in coating adhesion, comprising: hot-rolling a steel sheet, as a base sheet for coating, consisting of from 0.01 to 0.20% of C, from 0.030% or less of P, 0.010% or less of S, from 0.010 to 0.150% of Ti, 0.100% or less of sol. Al, less than 0.010% of N, from 0.0003 to 0.0100% of B, and at least one selected from the group consisting of from 0.01 to 1.00% of Si, from 0.10 to 2.50% of Mn, and from 0.05 to 1.00% of Cr, all in terms of percentage by mass, with the balance of Fe and unavoidable impurities; subjecting the base sheet for coating to a reduction heat treatment; and subjecting the base sheet for coating to hot-dip zinc alloy coating containing from 1.0 to 22.0% of Al and from 0.1 to 10.0% of Mg, all in terms of percentage by mass, with the balance of Zn and unavoidable impurities,
a coiling temperature in the hot-rolling step of the base sheet for coating being in a range of from 550 to 700° C., and in the reduction heat treatment, assuming that a period of time during which a temperature on a surface of the steel sheet is maintained to 750° C. to 860° C. in a furnace for the reduction heat treatment is designated as a retention time, and the maximum achieving temperature of the surface of the steel sheet in the furnace is designated as a reduction heat treatment temperature, performing the reduction heat treatment, at a reduction heat treatment temperature of from 750 to 860° C., for a retention time of 250 seconds or less in the case where the concentrations of Si and Mn in a portion within 4 μm from the surface of the steel sheet before the reduction heat treatment satisfy the condition A shown below, a retention time of 200 seconds or less in the case where the concentrations satisfy the condition B shown below, or a retention time of 150 seconds or less in the case where the concentrations satisfy the condition C shown below:concentrations of Si and Mn in a portion within 4 μm from the surface of the steel sheet before the reduction heat treatment (in terms of percentage by mass)A: 0.15% or less of Si and 0.8% or less of MnB: 0.6% or less of Si and 1.5% or less of Mn, but condition A not satisfiedC: more than 0.6% of Si and more than 1.5% of Mn. |