| 摘要 |
<p><P>PROBLEM TO BE SOLVED: To provide a crosslinkable resin for a fuel tank as a material for a large-sized container excellent in the balance of molding property and durability, especially the crosslinkable resin for the fuel tank, excellent in the balance of injection molding property, durability and impact resistance, and also excellent in fireproof performance, and a molded article by using the same. <P>SOLUTION: This crosslinkable resin for the fuel tank satisfies the conditions of (1) density before the crosslinking is≥0.940 and≤0.970 g/cm<SP>3</SP>, (2) melt flow rate before the crosslinking at 190°C under 2.16 kg load is≥0.1 and≤50 g/10 min, (3) Olsen bending stiffness after the crosslinking is≥600 and≤1,500 MPa and (4) gel fraction after the crosslinking is≥20%. The molded article by using the same is also provided. <P>COPYRIGHT: (C)2007,JPO&INPIT</p> |