| 摘要 |
A thermoplastic resin composition which comprises 30 to 99 wt% of a thermoplastic resin and 1 to 70 wt% of granulated fiber formed by granulating inorganic fibers having an average fiber diameter of 0.1 to 1.0 mu m, an aspect ratio of 50 to 300, and an oil absorption of 400 ml/100 g and above, said granulated fiber having an average diameter of 0.5 to 5 mm and a bulk density of 0.15 to 0.4. A process for producing a thermoplastic resin composition which comprises mixing in a mixer 30 to 99 wt% of a thermoplastic resin and 1 to 70 wt% of granulated fiber formed by granulating inorganic fibers having an average fiber diameter of 0.1 to 1.0 mu m, an aspect ratio of 50 to 300, and an oil absorption of 400 ml/100 g and above, said granulated fiber having an average diameter of 0.5 to 5 mm and a bulk density of 0.15 to 0.4. |