Austenitic alloy pipe and method for producing the same |
摘要 |
There is provided an austenitic alloy pipe that is durable even if a stress distribution different according to usage environment is applied. The austenitic alloy pipe in accordance with the present invention has a tensile yield strength YSLT of at least 689.1 MPa. The tensile yield strength YSLT, a compressive yield strength YSLC in a pipe axial direction, a tensile yield strength YSCT in a pipe circumferential direction of the alloy pipe, and a compressive yield strength YSCC in the pipe circumferential direction satisfy Formulas (1) to (4).
0.90≦YSLC/YSLT≦1.11 (1)0.90≦YSCC/YSCT≦1.11 (2)0.90≦YSCC/YSLT≦1.11 (3)0.90≦YSCT/YSLT≦1.11 (4) |
申请公布号 |
US9429254(B2) |
申请公布日期 |
2016.08.30 |
申请号 |
US201214006156 |
申请日期 |
2012.03.19 |
申请人 |
NIPPON STEEL & SUMITOMO METAL CORPORATION |
发明人 |
Sawawatari Naoki;Kuroda Kouichi;Suwabe Hitoshi;Ueyama Masaki |
分类号 |
C22C38/00;C21D9/08;C21D8/10;F16L9/02;C21D9/14;C22C38/02;C22C38/04;C22C38/42;C22C38/44;B21B19/06 |
主分类号 |
C22C38/00 |
代理机构 |
Clark & Brody |
代理人 |
Clark & Brody |
主权项 |
1. An austenitic alloy pipe, wherein
a tensile yield strength YSLT in a pipe axial direction of the alloy pipe is at least 689.1 MPa; and the tensile yield strength YSLT, a compressive yield strength YSLC in the pipe axial direction, a tensile yield strength YSCT in a pipe circumferential direction of the alloy pipe, and a compressive yield strength YSCC in the pipe circumferential direction satisfy Formulas (1) to (4).
0.90≦YSLC/YSLT≦1.11 (1)0.90≦YSCC/YSCT≦1.11 (2)0.90≦YSCC/YSLT≦1.11 (3)0.90≦YSCT/YSLT≦1.11 (4) |