Resin Coated Proppants and Process for the Preparation Thereof

摘要

The present invention provides a process for preparing resin coated highly spherical proppants of sizes 12/20 and 20/40 US mesh by sintering the calcined bauxite and then coating with resol type phenolic resin comprising phenol, m-cresol and formaldehyde. Coating is done without using any coupling or partitioning agent. The resin coated proppants prepared by the method of the present invention are useful in hydraulic fracturing of oil and gas producing formations. The prepared proppants have high acid resistance towards 3% HF-12% HCl mixture and have high crush resistance (upto 15000 psi) as per API specifications.

主权项

1. A process for the preparation of a resin coated proppant, said process comprising the steps of:
i. grinding raw calcined bauxite to obtain ground bauxite particles having a particle size in the range of 50 to 100 microns; ii. pelletizing said ground bauxite particles obtained in step (i) in a pelletizing machine by adding 5 to 10% water with the ground bauxite particles and rotating the machine for a period in the range of 5 to 15 minutes to obtain pellets; iii. sieving said pellets obtained in step (ii) to separate pellets having a size in the range of 425 to 850 microns; iv. air drying the separated pellets obtained in step (iii) for a period in the range of 24 to 36 hours to obtain dried pellets; v. sintering said dried pellets obtained in step (iv) at a temperature in the range of 1350 to 1450° C. for a period in the range of 30 to 35 minutes to obtain proppants; vi. dissolving 5 to 10% of a phenol-m-cresol-formaldehyde resin in a solvent to obtain a resin solution; vii. pouring the resin solution obtained in step (vi) on the proppants obtained in step (v) in a ratio ranging between 1:40 to 1:60 (w/w) with stirring for a period in the range of 30 to 35 minutes at a temperature in the range of 40 to 50° C. followed by drying and heating at a temperature in the range of 60 to 100° C. to obtain the resin coated proppants.