| 摘要 |
The present invention relates to a nylon film having high slip properties, in which a four-directional (MD, TD) strength value is 280 Mpa or higher, a thermal contraction rate (95°C water, 30 minutes) of 3% or lower, and a frictional coefficient of 0.3 or lower. The nylon film comprises 80-99 wt% of a nylon 6 resin (relative strength (RV) 3.3 or higher), 100-1,000 ppm of inorganic particles (A) having an average particle size of 2-3 μm, and 1,000-2,000 ppm of inorganic particles (B) having an average particle size of 1-2 μm. The inorganic particles (A) are selected from spherical silicone beads, gel silica, and spherical alumina silica, and the inorganic particles (B) contain kaolin. |