| 摘要 |
An application film which can be advantageously used as an intermediate transfer member in the application of a marking member to an adherend particularly in its complex three-dimensional area and, at the same time, has a good balance between softness, rubber elasticity, and stiffness. The film is constructed so that a backing film, when tested at a tensile speed of 200 mm/min according to the procedure set forth in JIS K 7127, has a 10 % modulus load of 0.3 to 1.6 kgf/15 mm, a 10 % modulus stress of 0.1 to 0.8 kgf/mm<2>, a 100 % modulus stress of 0.7 to 2.5 kgf/mm<2>, and a rate of change of modulus stress of not less than 3.0.
|