Reinforcement materials, suitable for the constitution of composite parts

摘要

The present invention concerns a new intermediate material to be associated with a thermosetting resin for making composite parts, consisting of a unidirectional layer of carbon fibers with a weight of 100 to 280 g/m2, associated on each of its faces, with a web of thermoplastic fibers having a thickness of 0.5 to 50 microns, preferably 3 to 35 microns, the intermediate material having a total thickness of 80 to 380 microns, preferably from 90 to 320 microns, and a process for manufacturing composite parts from such a material and the resulting composite parts.

主权项

1. An intermediate material, intended to be associated with a thermosetting resin for fabricating composite parts, said intermediate material having a first surface and a second surface, said intermediate material consisting of:
a unidirectional layer of carbon fibers with a surface density of 100 to 280 g/m2 and a thickness of between 90 and 270 microns, said unidirectional layer of carbon fibers having a first side and a second side; and a first web which comprises nonwoven thermoplastic fibers that have diameters of from 0.5 microns to 16 microns, said first web having an interior side located next to the first side of said unidirectional layer of carbon fibers and an exterior side which forms the first surface of said intermediate material, wherein said first web is thermally bonded to the first side of said unidirectional layer of carbon fibers and wherein the distance between the interior side and exterior side of said first web is from 3 to 15 microns; a second web which comprises nonwoven thermoplastic fibers that have diameters of from 0.5 microns to 16 microns, said second web having an interior side located next to the second side of said unidirectional layer of carbon fibers and an exterior side which forms the second surface of said intermediate material, wherein said second web is thermally bonded to the second side of said unidirectional layer of carbon fibers and wherein the distance between the interior side and exterior side of said second web is from 3 to 15 microns; and a plurality of surfaces which define a plurality of holes wherein each of said holes has a perimeter and wherein each of said holes extends from the first surface of said intermediate material to the second surface of said inter material to thereby form a plurality of perforations through said intermediate material and wherein said thermal bonding of said first and second webs to said layer of unidirectional carbon fibers is provided only by spot thermal bonding welds that are in the form discontinuous lines of spot welds which extend across the first and second surfaces said intermediate material.