Extrusion blow molded bottles |
摘要 |
Extrusion blow molded bottle comprising a propylene copolymer having a melt flow rate MFR2 (230° C.) of 2.0 to 6.0 g/10 min, a xylene cold soluble content of 20.0 to 40.0 wt.-%, and a comonomer content of more than 4.5 to 12.0 wt.-%, wherein the comonomer content of xylene cold soluble fraction of the extrusion blow molded article is of 16.0 to 28.0 wt.-%. |
申请公布号 |
US9394073(B2) |
申请公布日期 |
2016.07.19 |
申请号 |
US201314648079 |
申请日期 |
2013.12.10 |
申请人 |
Borealis AG |
发明人 |
Bernreitner Klaus;Klimke Katja |
分类号 |
B65D1/02;C08L23/14;C08L23/16;C08F210/06;B29C49/00;C08L23/10;B29C49/04;B29K23/00;C08L23/08;C08K5/00 |
主分类号 |
B65D1/02 |
代理机构 |
Tarolli, Sundheim, Covell & Tummino LLP |
代理人 |
Tarolli, Sundheim, Covell & Tummino LLP |
主权项 |
1. Extrusion blow molded article comprising at least 90 wt. % of a propylene copolymer based on the total amount of the extrusion blow molded article, wherein the propylene copolymer (PC) has:
(a) a melt flow rate MFR2 (230° C.) measured according to ISO 1133 in the range of 2.0 to 6.0 g/10min; (b) a xylene cold soluble content (XCS) determined according ISO 16152 (25° C.) in the range of 20.0 to 40.0 wt. %; (c) a comonomer content in the range of more than 4.5 to 12.0 wt. %; and (d) fulfills inequation (II):co(total)XCS≤0.35(II) wherein, Co (total) is the comonomer content [wt. %] of the propylene copolymer (PC), XCS is the content of the xylene cold soluble fraction (XCS) [wt. %] of the propylene copolymer (PC); wherein further; (e) the comonomer content of xylene cold soluble (XCS) fraction of the propylene copolymer (PC) is in the range of 12.0 to 28.0 wt. %. |