<p>The low thermal expansion and high rigidity ceramic sintered body of this invention is characterized by assuming as a crystal structure a hexagonal close-packed structure and substantially comprising solid solution crystal grains represented by the formula: MgaLibFecAldSieOf (wherein a is in the range of 1.8 to 1.9, b is in the range of 0.1 to 0.3, c is in the range of 0 to 0.2, d is in the range of 3.9 to 4.1, e is in the range of 6.0 to 7.0, and f is in the range of 19 to 23). It is further characterized by the solid solution crystal grains having lattice constants in the ranges, a0 in the range of 9.774 to 9.804 ANGSTROM and c0 in the range of 9.286 to 9.330 ANGSTROM , the relative density of the sintered body being of not less than 98%.</p> |