| 摘要 |
In a method for making a wrought nickel-chromium-molybdenum alloy having homogeneous, two-phase microstructures the alloy in ingot form is subjected to a homogenization treatment at a temperature between 2025°F and 2100°F, and then hot worked at start temperature between 2025°F and 2100°F. The alloy preferably contains 18.47 to 20.78 wt.% chromium, 19.24 to 20.87 wt.% molybdenum, 0.08 to 0.62 wt.% aluminum, less than 0.76 wt.% manganese, less than 2.10 wt.% iron, less than 0.56 wt.% copper, less than 0.14 wt.% silicon, up to 0.17 wt.% titanium, less than 0.013 wt.% carbon, and the balance nickel. |