| 摘要 |
Production of a nanocrystalline soft magnetic iron-silicon-boron alloy magnetic core involves crystallization heat treatment of the amorphous alloy at 150-400 degrees C in a transverse magnetic field of rectangular waveform. Production of a magnetic core of nanocrystalline soft magnetic alloy, containing more than 60 at.% Fe, 10-20 at.% Si, 0.1-2 at.% Cu, 5-20 at.% B and 0.1-10 at.% of one or more of Ti, Nb, Zr, Hf, V, Ta, Cr, Mo, W and Mn, the sum of Si + B being less than 30 at.%, involves crystallization heat treatment of the amorphous alloy to obtain a core having a maximum impedance magnetic permeability ( mu z) with a value of 350000 at 50 Hz and 25 degrees C and with a variation of less than 25% over the -25 to +100 degrees C range. The novelty is that the core is heat treated at 150-400 degrees C in a transverse magnetic field of rectangular waveform. |