A MARAGING STEEL ARTICLE AND METHOD OF MANUFACTURE.

摘要

A fully dense, powder-metallurgy produced maraging steel alloy article of prealloyed powder for use as a tool for high temperature applications. The article in the as-produced condition having a hardness less than 40 HRC to provide machinability and thereafter the article upon maraging heat treatment having a hardness greater than 45 HRC. A method for producing this article comprises compacting prealloyed powder to produce a fully dense article having a hardness less than 40 HRC and thereafter maraging heat treating to a hardness greater than 45 HRC.