| 摘要 |
The present invention proposes an austenitic high Mn stainless steel maintaining a hydrogen embrittlement resistance above that of SUS316L and adapted to a low temperature hydrogen environment by being designed in compositions to comprise, by mass%, C: 0.01 to 0.10%, N: 0.01 to 0.40%, Si: 0.1 to 1%, Cr: 10 to 20%, Mn: 6 to 20%, Cu: 2 to 5%, Ni: 1 to 6%, and a balance of Fe and unavoidable impurities and have an Md30 value of an indicator of an austenite stabilization degree satisfying -120<Md30<20, where Md30=497-462(C+N)-9.2Si-8.1Mn-13.7Cr-20(Ni+Cu)-18.5Mo |