发明名称 |
METHOD FOR PREPARING ULTRA-LONG-TUBE TYPE FINE-GRAIN MOLYBDENUM TUBE TARGET |
摘要 |
A method for preparing an ultra-long-tube type fine-grain molybdenum tube target uses molybdenum powder with the purity being greater than 3N to prepare a target tube with a uniform wall thickness, where the length is 1700-2700 mm; the diameter is greater than 150 mm; and the wall thickness is 15-40 mm. The method includes: taking molybdenum powder, feeding the molybdenum powder into a film, molding by static pressing, placing in a medium frequency furnace, performing hydrogen sintering to form a tube blank, placing into a mold, forging the mold of a tube target, placing into tempering furnace, annealing, forming fine-grain structures, fine processing, washing, and drying to prepare a molybdenum tube target. The method overcomes defects of a sintering process and a forging process, and relates to simple processes, easy industrial production and control, reduced pollution, reduced cost, improved quality, and remarkably improved production efficiency. |
申请公布号 |
US2016177437(A1) |
申请公布日期 |
2016.06.23 |
申请号 |
US201414759547 |
申请日期 |
2014.06.19 |
申请人 |
KEWEI MOLYBDENUM AND TUNGSTEN CO., LTD. |
发明人 |
ZHANG Lingjie |
分类号 |
C23C14/34;C22C27/04;B22F3/17;B22F1/00;B22F3/16 |
主分类号 |
C23C14/34 |
代理机构 |
|
代理人 |
|
主权项 |
1. A method for preparing an ultra-long-tube type fine-grain molybdenum tube target, wherein the method uses molybdenum powder with the purity being greater than 3N to prepare a target tube with a uniform wall thickness; the length is 1700-2700 mm; the diameter is greater than 150 mm; and the wall thickness is 15-40 mm, comprising:
(1) taking molybdenum powder having a granularity of 2.8-3.8 mm, feeding the molybdenum powder into a film prepared in advance, molding by static pressing under 160-200 Mpa, placing in a medium frequency furnace, sintering for 55-65 h under hydrogen protection at 1900-2000° C., sintering to form a tube blank, keeping the temperature, and reserving for use; (2) taking the sintered tube blank from the medium frequency furnace, placing into a mold prepared in advance, controlling the temperature of the tube blank to be 1350° C., forging the mold of a tube target, controlling the deformation amount of the tube blank to be less than 50% during the forging, and forging to form a tube target with the length being 1700-2700 mm, the diameter being greater than 150 mm, and the wall thickness being 15-40 mm; (3) taking the tube target formed by forging, placing in a tempering furnace of 1000-1200° C., annealing for 1-3 h, and stabilizing fine-grain structures; and (4) performing fine processing on the tube target, washing, and drying to prepare the fine-grain molybdenum tube target. |