发明名称 |
METHOD FOR RESTORING THE STRUCTURE OF A STEEL COMPONENT AFTER HEATING AND STEEL COMPONENT OBTAINED BY THE METHOD |
摘要 |
The present disclosure relates to a method for restoring a steel structure for a steel component, such as a soft annealed steel component, a welding joint comprising the steps of welding the steel component to form a welding joint, quenching the steel component to a temperature of above the martensite start temperature (Ms) and maintaining the steel component at that temperature for a holding time sufficient for transformation of all austenite, re-heating the steel component to a temperature of 950 to 1110° C., quenching the steel component to a temperature of above the martensite start temperature (Ms) to form bainite, and maintaining the steel component at that temperature for a holding time sufficient for transformation of all austenite to bainite, re-heating the steel component to a temperature of at least 580° C. but below the Ac1 transformation temperature, and maintaining the steel component at that temperature for a holding time sufficient for the steel component to exhibit Brinell hardness number of between 215 and 320 HB10/3000, and cooling the steel component. |
申请公布号 |
US2016348206(A1) |
申请公布日期 |
2016.12.01 |
申请号 |
US201615163729 |
申请日期 |
2016.05.25 |
申请人 |
Aktiebolaget SKF |
发明人 |
Larsson Staffan |
分类号 |
C21D9/40;C21D8/10;C21D1/613;C21D1/607;C21D1/60;C21D1/78;B23K11/04;C22C38/60;C22C38/50;C22C38/44;C22C38/42;C22C38/06;C22C38/04;C22C38/02;C22C38/00;C21D9/50 |
主分类号 |
C21D9/40 |
代理机构 |
|
代理人 |
|
主权项 |
1. A method for restoring a steel structure for a steel component after heating characterized in that it comprises the steps of:
a) heating a steel component to a temperature of at least 1100° C., b) quenching the steel component to a temperature above the martensite start temperature (Ms) and maintaining the steel component at that temperature for a holding time sufficient for transformation of all austenite, c) re-heating the steel component to a temperature of 950 to 1110° C., d) quenching the steel component to a temperature above the martensite start temperature (Ms) to form bainite, and maintaining the steel component at that temperature for a holding time sufficient for transformation of all austenite to bainite, e) re-heating the steel component to a temperature of at least 580° C. but below the Ac1 transformation temperature, and maintaining the steel component at that temperature for a holding time sufficient for the steel component to exhibit Brinell hardness number of between 215 and 320 HB10/3000, f) cooling the steel component. |
地址 |
Goteborg SE |