<p>It is an obj ect of the present invention to provide a coated steel sheet, properties of which such as an adhesion property to a substrate and press oil resistance are improved. A coated steel sheet coated with a composite coat,
wherein said composite coat is a coat formed by compounding ethylene-unsaturated carboxylic acid copolymerization resin particles (A) having an average particle diameter of 20 to 100 nm and a silanol group and/or an alkoxysilyl group, silicon oxide particles (B) having an average particle diameter of 5 to 50 nm and an organic titanium compound (C), and