Foils from homo- and copolymers of propene having a thickness of 100-200 microns are heated to a temperature between the glass transition temperature and the crystalline melting point and are deformed without using a plunger or die to a deepness to diameter ratio of at least 0.4, using a mould having a temperature of at most 25 DEG C. |