摘要

Thermoplastic polyphosphonatocarbonate prepared by polycondensing at least one aromatic dihydroxy compound with a diaryl carbonate and a phosphonic acid diaryl ester in the presence of a basic polycondensation catalyst at a temperature of from 80 DEG to 340 DEG and under a pressure of 600 to 0.1 mm Hg in an inert gaseous atmosphere, the molar ratio of diaryl carbonate to phosphonic diaryl ester being from 5:95 to 95:5 and the molar ratio of aromatic dihydroxy compound to the sum of diaryl carbonate and phosphonic acid diaryl ester being from 0.91:1 to 0.99:1, and following polycondensation, neutralizing said basic catalyst.