Powder or lengths of ceramic or metallic superconductor ceramic compositions are loaded into lengths of metal tubing. Mechanical reduction of filled tubing is facilitated by use of elevated temperatures and intermittent heat treatments as required. Rolling to a flattened cross section aids bending to the final device configurations and subsequent hot-isostatic-pressing. Hot-isostatic-pressing steps (1) close defects, including voids, cracks and joints and improve microstructure, and (2) join tested wire lengths to produce a superconductor length in the final configuration. Encapsulation of the superconductor is completed and assured with metal sleeves and solder or glass.
|