发明名称 |
Method for producing high strength Cu-Ni-Sn alloy containing manganese |
摘要 |
A high strength Cu-Ni-Sn alloy, comprising 3-25% Ni, 3-9% Sn, 0.05-1.5% Mn, balance Cu, is heated to a temperature of 800 DEG C. or above in a single-phase region. This heat treatment is followed by quenching and subsequent heating at a temperature range of 600 DEG -770 DEG C. in a two-phase region, followed by quenching and a finishing process with a ratio of 0-60%. Thereafter, the processed alloy is subjected to a final heat-treatment at a temperature of 350 DEG -500 DEG C.
|
申请公布号 |
US5019185(A) |
申请公布日期 |
1991.05.28 |
申请号 |
US19890436737 |
申请日期 |
1989.11.15 |
申请人 |
MITSUBISHI DENKI KABUSHIKI KAISHA |
发明人 |
NAKAJIMA, TAKASHI;KUBOZONO, KENJI;MORI, TOSHIHIKO;ITO, TAKEFUMI;HASHITSUME, KIMIO;IWASE, SHINICHI |
分类号 |
C22C9/06;C22F1/00;C22F1/08 |
主分类号 |
C22C9/06 |
代理机构 |
|
代理人 |
|
主权项 |
|
地址 |
|