| 摘要 |
A ferritic stainless steel sheet which has not only superior high-temperature fatigue characteristics, but also superior workability at room temperatures. The steel sheet contains, by weight percent, C: not more than 0.02%, Si: 0.2 to 1.0%, Mn: not more than 1.5%, Cr: 11.0 to 20.0%, Ni: 0.05 to 2.0%, Mo: 1.0 to 2.0%, Al: not more than 1.0%, Nb: 0.2 to 0.8%, and N: not more than 0.02%, balance essentially Fe, and an aspect ratio (dRD/dTD) of grain size in planes at ¼ and ¾ sheet thickness, seen a direction normal to a sheet surface, in the range of 1.03 to 1.35. The steel sheet has a thickness greater than 0.3 mm but not greater than 2.5 mm, and a yield strength Y.S.<=360 MPa and an r-value>=1.3 at 30° C., and wherein after maintaining the steel sheet at 90° C. for one hour, the Y.S.>=18.0 MPa.
|