| 摘要 |
PROBLEM TO BE SOLVED: To obtain an olefin-based resin composition excellent in film see- through feeling, balance between transparency, appearance and blocking resistance, etc., and good in secondary processability including slipperiness, scratch resistance and roll staining resistance as well. SOLUTION: This resin composition is obtained by incorporating (A) 100 pts.wt. of an olefin-based resin with (B) 0.01-2.0 pts.wt. of an antiblocking agent; wherein the component B is composed of 40-90 wt.% of an antiblocking agent B1 with a weight-average particle size of >=1.5μm but <4.0μm and an antiblocking agent B2 with a weight-average particle size of 4.0-7.0μm with the contents of the particles with a size >=1.5 times each of the weight-average particle size being <10 wt.%, respectively, and the difference between the weight-average particle size of the antiblocking agent B1 and that of the antiblocking agent B2 being >=0.5μm but <3.0μm.
|