<P>PROCEDE DE FABRICATION D'UNE PLAQUE DE VERRE QUI EST TRANSPARENTE DANS AU MOINS UNE DIRECTION ET OPAQUE DANS AU MOINS UNE AUTRE DIRECTION.</P><P>A PARTIR DU MELANGE AYANT LA COMPOSITION SUIVANTE (EN POIDS): SIO: 78,7; BO: 0,2; ALO: 4,2; LIO: 9,5; NAO: 1,7; KO: 4,0; ZNO: 1,0; AGCL: 0,2; CEO: 0,03; SBO: 0,5; ON PREPARE PAR FUSION A DES TEMPERATURES D'ENVIRON 1500C UN VERRE PHOTOSENSIBLE AVEC LEQUEL ON FABRIQUE UNE PLAQUE 53 DE 2 A 3MM D'EPAISSEUR D. ON RECOUVRE CETTE PLAQUE D'UN MASQUE 52 INTERROMPU DE MINCES BANDES B EQUIDISTANTES (DISTANCE C), ET ON L'IRRADIE AVEC UN FAISCEAU 51 DE LUMIERE ULTRAVIOLETTE, AUSSI PARALLELE QUE POSSIBLE, EMANANT D'UNE LAMPE A VAPEUR DE MERCURE A HAUTE PRESSION. PAR LE TRAITEMENT THERMIQUE SUBSEQUENT LES BANDES IRRADIEES SONT TRANSFORMEES EN VITROCERAMIQUE.</P><P>APPLICATION POUR ELEMENTS ANTIREFLEXION ET ANTIEBLOUISSEMENT, SURTOUT POUR DISPOSITIFS D'AFFICHAGE A CRISTAUX LIQUIDES.</P>
|