摘要 |
The present invention relates to a Ni base alloy having sufficient strength at high temperatures and high corrosion resistance at high temperatures in a high-temperature composite corrosive environment in which chlorination or sulfidation occurs simultaneously with high-temperature oxidation, without excessive cooling or surface protection. According to the present invention, a Ni base alloy having high-temperature strength and corrosion resistance includes Cr in a range of from 25 to 40 weight %, Al in a range of from 1.5 to 2.5 weight %, C in a range of from 0.1 to 0.5 weight %, W of 15 weight % or less, Mn of 2.0 weight % or less, Si in a range of from 0.3 to 6 weight %, Fe of 5 % or less, and Ni of rest except inevitable impurities. When strength at high temperatures is allowed to be small, W is in a range of from 0 to 8 %, and Si is in a range of from 0.3 to 1 % or from 1 to 6 %. In order to enhance strength at high temperatures, W is in a range of from 8 to 15, and Si is in a range of from 0.3 to 1 % or from 1 to 6 %. <IMAGE> |