发明名称 |
STEEL SHEET FOR CROWN CAP, METHOD FOR MANUFACTURING SAME, AND CROWN CAP |
摘要 |
A steel sheet for crown caps includes C: 0.0005 to 0.0050%, Si: 0.020% or less, Mn: 0.10 to 0.60%, P: 0.020% or less, S: 0.020% or less, Al: 0.01 to 0.10%, N: 0.0050% or less, Nb: 0.010 to 0.050%, and Fe and inevitable impurities. The steel sheet has an average r value of 1.30 or more and a YP of 450 MPa or more and 650 MPa or less. The steel sheet is obtained by hot rolling a steel slab at a slab reheating temperature of 1,150° C. or higher and a finishing temperature of 870° C. or higher; coiling the hot rolled steel sheet at a coiling temperature of 600° C. or higher, performing pickling; then-performing primary cold rolling; performing annealing at an annealing temperature of recrystallization temperature or more and 790° ° C. or less; and performing secondary cold rolling at a rolling reduction of 10% or more and 50% or less. |
申请公布号 |
US2016362761(A1) |
申请公布日期 |
2016.12.15 |
申请号 |
US201515121540 |
申请日期 |
2015.02.13 |
申请人 |
JFE STEEL CORPORATION |
发明人 |
HIRAGUCHI Tomonari;KOJIMA Katsumi;NAKAMURA Hiroki;TSUJIMOTO Masami;KIKUCHI Toshihiro |
分类号 |
C21D9/46;C22C38/06;C22C38/04;B65D41/12;C22C38/00;C21D8/02;C23G1/00;C22C38/12;C22C38/02 |
主分类号 |
C21D9/46 |
代理机构 |
|
代理人 |
|
主权项 |
1. A steel sheet for crown caps, the steel sheet comprising:
C: 0.0005 to 0.0050%, by mass %: Si: 0.020% or less, by mass %: Mn: 0.10 to 0.60%, by mass %: P: 0.020% or less, by mass %; S: 0.020% or less, by mass %: Al: 0.01 to 0.10%, by mass %: N: 0.0050% or less, by mass %: Nb: 0.010 to 0.050%, by mass %; and Fe and inevitable impurities, wherein the steel sheet has an average r value of 1.30 or more and a YP of 450 MPa or more and 650 MPa or less. |
地址 |
Tokyo JP |