1. A process for the production of a dialysis membrane of regenerated cellulose in the form of flat films, tubular films or hollow filaments, characterized in that a mixture of from 7 to 25 % by weight of cellulose, from 93 to 50 % by weight of tertiary amine oxide, optionally up to 25 % by weight of a diluent which does not dissolve the cellulose and up to 10 % by weight of standard additives, based in each case on the weight of the spinning solution, is dissolved in less than 8 minutes at temperatures of from 80 to 150 degrees C in a mixing unit, in that the solution is degassed, extruded through a wide slot die, annular slot die or hollow filament die into a precipitation bath, washed and, after addition of plasticizer, is dried without shrinkage at temperatures of from 50 to 110 degrees C and wound into roll form. |