摘要 |
<p>A method for producing a hot-rolled electrical steel sheet excellent in magnetic characteristics and corrosion resistance, characterized in that the method comprises providing heating a super high purity iron having the composition: Fe: 99.95 mass % or more, C + N + S: 10 mass ppm or less, 0: 50 mass ppm or less, and balance: inevitable impurities, heating the iron to the gamma region thereof, carrying out a hot rolling at the gamma region under a condition wherein a total draft is 50 % or more and the friction coefficient between a roll and a rolled material is 0.3 or less at least in one pass, and then cooling the rooled iron under a condition wherein the average cooling speed in the range of Ar3 transformation point to 300 DEG C is 0.5 to 150 DEG C/min, thereby forming orientation grains having <100> axes integrated to the direction perpendicular to a sheet plane.</p> |