发明名称 |
Weld metal having excellent temper embrittlement resistance |
摘要 |
A weld metal according to the present invention has a specific chemical composition, contains carbide particles each having an equivalent circle diameter of greater than 0.5 μm in a number of 0.25 or less per micrometer of grain boundary length, and has an A-value as specified by Formula (1) of 0.12 or more, Formula (1) expressed as follows:
A-value=([V]/51+[Nb]/93)/([Cr]/52+[Mo]/96) (1)
where [V], [Nb], [Cr], and [Mo] are contents (percent by mass) of V, Nb, Cr, and Mo, respectively, in the weld metal. |
申请公布号 |
US9505087(B2) |
申请公布日期 |
2016.11.29 |
申请号 |
US201214350985 |
申请日期 |
2012.11.21 |
申请人 |
Kobe Steel, Ltd. |
发明人 |
Nako Hidenori;Yamashita Ken;Otsu Minoru;Taniguchi Genichi;Sakata Mikihiro |
分类号 |
C22C38/22;C22C38/24;C22C38/26;B23K35/22;B23K35/30;B23K9/23;C22C38/54;C22C38/00;C22C38/02;C22C38/04;C22C38/06;C22C38/20;C22C38/32;C22C38/34;C22C38/38;C22C38/42;C22C38/44;C22C38/46;C22C38/48;B23K35/365;C21D9/50;B23K35/36;C22C38/50;B23K35/02 |
主分类号 |
C22C38/22 |
代理机构 |
Oblon, McClelland, Maier & Neustadt, L.L.P. |
代理人 |
Oblon, McClelland, Maier & Neustadt, L.L.P. |
主权项 |
1. A weld metal, comprising: in percent by mass,
C in a content of 0.05% to 0.15%; Si in a content of 0.1% to 0.50%; Mn in a content of 0.60% to 1.30%; Cr in a content of 1.80% to 3.0%; Mo in a content of 0.80% to 1.20%; V in a content of 0.25% to 0.50%; Nb in a content of 0.010% to 0.050%; N in a content of greater than 0% to 0.025%; O in a content of 0.020% to 0.060%, and; wherein the weld metal comprises carbide particles each having an equivalent circle diameter of greater than 0.5 μm in a number of 0.25 or less per micrometer of grain boundary length; and the weld metal has an A-value as specified by Formula (1) of 0.12 or more;
A-value=([V]/51+[Nb]/93)/([Cr]/52+[Mo]/96) (1)where [V], [Nb], [Cr], and [Mo] are contents, in percent by mass, of V, Nb, Cr, and Mo, respectively, in the weld metal. |