发明名称 |
High rigidity rubber material |
摘要 |
The present invention relates to a rubber material containing an EPDM rubber composition containing an EPDM rubber, a carbon black, a softening agent, a vulcanizing agent and a sulfur compound, in which a blending amount of whole components from which the vulcanizing agent and the sulfur compound are excluded is from 300 to 400 parts by weight, and a total sulfur blending amount is from 1.0 to 2.8 parts by weight, in which a blending ratio of carbon black/softening agent is from 1.8 to 2.5, and in which the EPDM rubber composition has a Mooney viscosity of from 70 to 100 at 100° C., and a vulcanized composition thereof has a rate of rigidity change satisfying the following equation (1):
{(30% Modulus at 100° C./30% modulus at 23° C.)−1}×100%≧−10% (1). |
申请公布号 |
US9493628(B2) |
申请公布日期 |
2016.11.15 |
申请号 |
US201213659669 |
申请日期 |
2012.10.24 |
申请人 |
TOYODA GOSEI CO., LTD. |
发明人 |
Kurimoto Hidekazu;Yamaguchi Hiroshi;Nakashima Naomi |
分类号 |
C08L23/16;C08K5/00 |
主分类号 |
C08L23/16 |
代理机构 |
Posz Law Group, PLC |
代理人 |
Posz Law Group, PLC |
主权项 |
1. A rubber hose material made of an EPDM rubber composition, the EPDM rubber composition consisting essentially of:
100 parts by weight of an EPDM rubber blended together with: 135 to 180 parts by weight carbon black; 55 to 100 parts by weight a softening agent; a blending ratio of carbon black/softening agent being from 1.8 to 2.5; 0.4 to 1.5 parts by weight of powdered sulfur as a vulcanizing agent; 0.4 to 0.9 parts by weight of sulfur contained within a sulfur compound selected from the group consisting of sulfur compounds that release sulfur at the time of vulcanization; 1.0 to 1.7 parts by weight of a total sulfur blending amount, the total sulfur blending amount including the weight of the powdered sulfur and the weight of the sulfur contained within the sulfur compound; and a blending amount of all components of the EPDM rubber composition from which the powdered sulfur as a vulcanizing agent and the sulfur compound are excluded is from 300 to 400 parts by weight, wherein the EPDM rubber composition has a Mooney viscosity of 100 at 100° C., and a vulcanized composition thereof has a rate of rigidity change satisfying the following equation (1):
{(30% Modulus at 100° C./30% modulus at 23° C.)−1}×100%≧−10% (1). |