Desulfurizer For Conversion And Absorption Of High-Concentration Carbonyl Sulfide And A Desulfurizer For Catalytic Conversion And Absorption Of Carbon Disulfide And Their Preparation Methods |
摘要 |
Provided is a high-concentration carbonyl sulfide conversion-absorption type desulfurizer for use at medium-low temperature and preparation method thereof. The desulfurizer comprises 50%-75% magnetic iron oxide red (Fe21.333O32), 5%-10% alkali metal oxide (K2O), 5-35% anatase TiO2, and 5-10% shaping binder. The method of preparing the desulfurizer comprises: uniformly mixing a metatitanic acid prepared using ferrous sulfate recycled as a by-product from titanium dioxide production with K2CO3, calcining to activate at 500° C.-700° C., mixing with the magnetic iron oxide red and binder, roll molding at room temperature to form balls which are dried at 100° C.-150° C. to obtain the desulfurizer. The desulfurizer has a hydrolysis conversion of carbonyl sulfide higher than 99%, and has a higher sulfur capacity more than 25%. |
申请公布号 |
US2016325226(A1) |
申请公布日期 |
2016.11.10 |
申请号 |
US201415108968 |
申请日期 |
2014.12.30 |
申请人 |
BEIJING SJ ENVIRONMENTAL PROTECTION AND NEW MATERIAL CO., LTD. |
发明人 |
Li Liying;SONG Wenwen;MAO Wenjun;ZHANG Zhimin;LIU Boshu;Liu Zhenyi |
分类号 |
B01D53/80;B01J21/16;B01J23/78;B01J37/00;B01J37/04;B01J20/30;B01J37/06;B01J20/12;B01J20/04;B01J20/08;B01J20/02;B01D53/48;B01J37/08 |
主分类号 |
B01D53/80 |
代理机构 |
|
代理人 |
|
主权项 |
1. A desulfurizer for conversion and absorption of high-concentration carbonyl sulfide, comprising:
magnetic iron oxide red Fe21.333O32 in an amount of 50-75 parts by weight; K2O in an amount of 5-10 parts by weight; anatase-type TiO2 in an amount of 5-35 parts by weight; and a binder in an amount of 5-10 parts by weight. |