| 摘要 |
Provided are: a high-strength steel sheet which is improved in both elongation and local formability and thus exhibits excellent workability; and a manufacturing method thereof. The high-strength steel sheet contains C, Si, Mn, Al, P and S with the remainder including iron and unavoidable impurities, and has a metal structure which includes polygonal ferrite, bainite, tempered martensite, and retained austenite. In the metal structure, (1) the bainite has a composite microstructure including both a high-temperature-formed bainite having an average distance between adjacent regions of retained austenite and/or carbide of 1 μm or more and a low-temperature-formed bainite having an average distance between adjacent regions of retained austenite and/or carbide of less than 1 μm each identified upon observation with a scanning electron microscope; and (2) the retained austenite is present in a volume percentage of 5% or more of the entire metal structure as determined by a saturation magnetization measurement. |