| 摘要 |
Morphologically improved cerium oxide particulates having low sulfur content, useful, e.g., as catalysts/catalyst supports, and having a B.E.T. specific surface of at least 85+/-5 m2/g, measured at a temperature ranging from 350 DEG C. to 500 DEG C., are prepared by reacting an aqueous solution of cerium (IV) salt with an aqueous solution of sulfate ions to precipitate a basic ceric sulfate, filtering the precipitate which results, washing and optionally drying said precipitate, and then calcining same. |