Manufacturing process for rice husk fiber synthetic resin powder and rice husk fiber product

摘要

A manufacturing process for rice husk fiber synthetic resin powder includes grinding rice husks into rice husk powder, feeding the powder into a mixer, adding and uniformly mixing cellulose, starch, and water, removing and cooling the mixture into rice husk fiber powder; additionally putting natural resin and lignin into a reaction kettle, adding water and agitating uniformly into slurry, adding nano-silica and continuing agitating evenly, and after cooling, adding the rice husk fiber powder and continuing the agitation, cooling and removing the mixture, thus obtaining a paste material; and injecting the paste material into a flash drier to produce rice husk fiber synthetic resin powder. The rice husk fiber synthetic resin powder can be used to make rice husk fiber products such as tableware, toys, furniture and kitchenware that have good physical properties and are degradable into organic fertilizer, thereby being environmentally friendly and commercially promising.

主权项

1. A manufacturing process for rice husk fiber synthetic resin powder, being characterized in comprising the following steps:
(1) grinding 20-80 wt. % rice husk into fine rice husk powder having a mesh size of 50-300; (2) feeding the rice husk powder of step (1) into a high-speed heating mixer, adding 5-35 wt. % cellulose and 5-40 wt. % starch, mixing well while introducing 10-35 wt. % water, removing the mixture from the high-speed heating mixer, letting the mixture to cool, and thereby obtaining rice husk fiber powder; (3) placing 15-35 wt. % natural resin and 65-85 wt. % lignin into a reaction kettle, adding 10-20 wt. % water into the reaction kettle, agitating the mixture uniformly into slurry, heating the mixture to 100-300° C., then adding 5-15 wt. % nano-silica, mixing the mixture uniformly, cooling the reaction kettle to a temperature below 120° C., adding 20-80 wt. % rice husk fiber powder while mixing, removing the mixture from the reaction kettle, and thereby obtaining a paste material; (4) pouring the paste material of step (3) into a flash drier, drying the paste material with heat airflow of 60-120° C., removing the dried paste material from the flash drier when it has a moisture content of 5-15%, and thereby obtaining brownish-yellow rice husk fiber synthetic resin powder; and (5) cooling the rice husk fiber synthetic resin powder of step (4) and packaging the cooled powder for storage as a final product of the rice husk fiber synthetic resin powder.