Braze alloy compositions and brazing methods for superalloys

摘要

A multi-component braze filler alloy comprising 60-70% by weight CM247 superalloy and BRB braze alloy is diffusion brazed to a CM247 alloy base substrate, such as a gas turbine blade or vane. The substrate/braze interface may be subsequently weld-repaired without de-melting and migrating the braze alloy from the interface. The weld zone and surrounding area are solidification crack resistant. After the alloy composition is brazed to the base substrate the component may be returned to service. Thereafter the component remains repairable by welding or re-brazing, if needed to correct future in-service defects.

主权项

1. A method for brazing a Ni base superalloy component comprising, in the following order:
placing the Ni base superalloy component to be brazed and the brazing material into a brazing furnace, properly configured to perform the desired brazing process upon heating; and increasing the furnace temperature to within about 25 deg. F of 1800 deg. F at a rate of approximately 28 deg. F per minute; and reducing the pressure within the furnace to less than about 0.005 Torr and hold for stabilization; and increasing the furnace temperature to within about 12 deg. F of 2270 deg. F at a rate no greater than about 10 deg. F per min. and hold at this temperature for about 240 to 255 minutes for combined braze and diffusion cycle time while maintaining the pressure no greater than about 0.005 Torr; and vacuum cooling the furnace temperature to within about 25 deg. F of 1975 deg. F in a time no more than about 3 minutes; and rapid cooling to room temperature by back purging with inert gas; and wherein the brazing material comprises a mixture of a base alloy comprising, by weight: C: XC=0.07-0.15%; Cr: XCr=8.1-8.4%; Co: XCo=9.2-10.0%; Al: XAl=5.5-5.6%; B: XB=0.015%; W: Xw=9.5-10.0%; Mo: XMo=0.5-0.7%; Ta: XTa=3.0-3.2%; Ti: XTi=0.7-1.0%; Hf: XHf=1.4-1.5%; Zr: XZr=0.015-0.05%; Ni: XNi=(balance) in the range from approximately 60% to 70% by weight and the balance comprises a braze alloy comprising: Cr: XCr=13.0-14.0% Co: XCo=9.0-10.0% Al: XAl=3.5-4.5% B: XB=2.25-2.75% Ni: XNi=(balance).