Method for preparing fluorine/nitrogen co-doped graphitized carbon microspheres with high volumetric specific capacitance

摘要

The present invention provides a method for preparing fluorine/nitrogen co-doped graphitized carbon microspheres with high volumetric specific capacitance, which is a simple process with moderate reaction conditions, high reproducibility, and low costs. The fluorine/nitrogen co-doped graphitized carbon microspheres prepared according to the present invention have a very high density, exhibit good electrochemical properties in an alkaline environment, as well as very high volumetric specific capacitance and good cyclic stability, and is of great importance in improving the properties of the electrode material for a capacitor.

主权项

1. A method for preparing fluorine/nitrogen co-doped graphitized carbon microspheres, wherein:
16%-82% of a carbon source, 13%-71% of a nitrogen source, 3%-17% of a fluorine source, and 1%-18% of a surfactant, all in a mass percentage, are successively added to a reactor under a nitrogen atmosphere, and stirred for 10-30 minutes before the reactor is sealed; the reactor is placed into a crucible furnace and heated at 300-600° C. for 6-48 hours, followed by naturally cooling the reactor to room temperature and removing the reaction mixture therefrom; the resulted reaction mixture is washed successively with absolute ethanol, 0.1 M-5 M diluted hydrochloride acid and distilled water for 3-6 times, and filtered; and powder thus obtained is placed into a vacuum oven and dried in vacuum at 60-100° C. for 6-12 hours.