Non-solidifying rubberized asphalt composition for providing inpermeable intermediate drainage layer and method for providing inpermeable intermediate drainage layer with single paving process using the same

摘要

The present invention relates to a paving method of forming an intermediate layer, where a non-solidifying rubberized asphalt penetrates, on an asphalt mixture for base layer or a cement concrete to provide a permeable layer and an impermeable (intermediate) layer simultaneously with a single paving process for surface layer. The waterproofing and draining functions of the non-solidifying rubberized asphalt layer completely block water or moisture from penetrating into the underlying layer and protect the roads from damage due to freezing temperature with the moisture penetrating into the group in winter. The non-solidifying rubberized asphalt layer constituting the intermediate layer has the non-solidifying rubberized asphalt melt down and move upwards under the paving temperature and pressure applied during the paving process of forming a surface layer and firmly bind with the base layer, thereby completing an integrated pavement structure with enhanced water resistance and durability.

主权项

1. A drainage asphalt composite paving method, which can be used to form an impermeable intermediate layer and a drainage surface layer with a single paving process, the method comprising:
(1) laying a non-solidifying rubberized asphalt composition to a thickness of 2 to 8 mm on the surface of a surface-cut asphalt, cement concrete or base layer; (2) applying sand on the non-solidifying rubberized asphalt composition laid in the step (1); and (3) laying a mixture for drainage surface layer on the sand applied in the step (2) and performing a tamping, wherein the non-solidifying rubberized asphalt composition comprises 80 to 90 wt. % of asphalt having a penetrability of 60 to 80, 5 to 15 wt. % of a modifier, 3 to 10 wt. % of a process oil, 0.5 to 4 wt. % of a strength reinforcing agent, 0.1 to 1 wt. % of an additive, 0.1 to 1 wt. % of an antioxidant, and 0.1 to 0.5 wt. % of an interlayer adherence promoter, and has a viscosity of 3,000 to 100 cP at temperature of 130 to 170° C., and wherein the tamping process of the step (3) allows the non-solidifying rubberized asphalt composition to penetrate into the drainage surface layer and form the impermeable drainage intermediate layer.