Superhydrophobic nanotextured polymer and metal surfaces

摘要

A method of manufacturing a multiscale (hierarchical) superhydrophobic surface is provided. The method includes texturing a polymer surface at three size scales, in a fractal-like or pseudo-fractal-like manner, the lowest scale being nanoscale and the highest microscale. The hydrophobic polymer surface may be converted to hydrophobic metal surface by subsequent deposition of a metal layer onto the polymer surface.

主权项

1. A method of manufacturing a hydrophobic surface having an apparent contact angle of at least 150°, the method comprising:
i) providing a base substrate and a polymeric material; ii) forming a layer of said polymeric material on said substrate, said layer having a bottom surface attached to said substrate base, and an upper surface, wherein the polymeric material in said layer is structured at two different size scales, the first scale ranging from about 0.1 to 2 μm, and the second scale between 0.5-50 μm; and iii) further structuring said polymeric material at a third size scale by forming indentations on said upper surface, wherein an average distance between adjacent indentations is from 20 to 200 μm,wherein the hydrophobic surface having the three size scales is arranged in pseudoperiodic areas of higher and lower mass density, measured along a line going through the polymeric material and oscillating in a fractal-like manner; thereby obtaining a hydrophobic surface having an apparent contact angle of at least 150°.