发明名称 |
Low-density steel having good drawability |
摘要 |
The invention relates to a hot-rolled ferritic steel sheet, the composition of the steel of which comprises, the contents being expressed by weight: 0.001≦C≦0.15%, Mn≦1%, Si≦1.5%, 6%≦Al≦10%, 0.020%≦Ti≦0.5%, S≦0.050%, P≦0.1%, and, optionally, one or more elements chosen from: Cr≦1%, Mo≦1%, Ni≦1%, Nb≦0.1%, V≦0.2%, B≦0.010%, the balance of the composition consisting of iron and inevitable impurities resulting from the smelting, the average ferrite grain size dIV measured on a surface perpendicular to the transverse direction with respect to the rolling being less than 100 microns. |
申请公布号 |
US9580766(B2) |
申请公布日期 |
2017.02.28 |
申请号 |
US200812600085 |
申请日期 |
2008.04.29 |
申请人 |
ArcelorMittal France |
发明人 |
Perlade Astrid;Garat Xavier;Uriarte Jean-Louis;Bouaziz Olivier;Drillet Josee |
分类号 |
C21D8/02;C21D8/04;C22C38/06;C22C38/14;C21D6/00 |
主分类号 |
C21D8/02 |
代理机构 |
Davidson, Davidson & Kappel, LLC |
代理人 |
Davidson, Davidson & Kappel, LLC |
主权项 |
1. A hot-rolled ferritic steel sheet, the composition of the steel of which comprises, the contents being expressed by weight:
0.001≦C≦0.15% Mn≦1% Si≦1.5% 7.5%≦Al≦10% 0.020%≦Ti≦0.5% S≦0.050%, and P≦0.1%the balance of the composition consisting of iron and inevitable impurities resulting from the smelting, wherein said hot-rolled ferritic steel sheet, resulting from hot-rolling of said steel composition, comprises kappa (κ) precipitates and non-equiaxed ferrite grains wherein an average grain size div of the non-equiaxed ferrite grains, measured on a surface perpendicular to the transverse direction with respect to the hot-rolling is less than 100 microns and wherein the non-equiaxed ferrite grains have an elongation in a direction of the hot rolling. |